Diamond tools solutions
1.JF-01
Components: Fe Cu
Theoretical Density: 8.16g/cm3
Sintering Temperature: 830鈩
Bending Strength: 1350MPa
Hardness: 98-102HRB
HApplication & Feature: Suitable for making multiple diamond tools, added as
a basic powder
to lower the cost, diamond embedded well in the matrix, sharpness.
2.HYF-06
Components: Fe Cu Ni Sn
Theoretical Density: 8.05g/cm3
Sintering Temperature: 830鈩
Bending Strength: 1100MPa
Hardness: 105-110HRB
Application & Formula:
Edge-grinding wheel and roller blade for processing ceramics:
(65-70)%HYF-06 + (10-20)%Fe + (10-20)%Cu + (1-2)%Sn + (3-7)%Ni + (1-2)%Ti,
Ratio of Diamond: 20-25% (25% 40/45 + 50% 50/60 + 25%60/70)
Sintering Temperature: 780鈩
3.JF-26
Components: Fe Cu Ni
Theoretical Density: 8.23g/cm3
Sintering Temperature: 850鈩
Bending Strength: 1400MPa
Hardness: 108-112HRB
Application & Formula:
Medium and high quality concrete high speed blade
60%JF-26 + (10-12)%Co + 15%Cu + 2%Sn + (3-5)%No(CO)4 + residue Fe
Ratio of Diamond: 25-28% (20% 40/45 + 50% 45/50 + 30%50/60)
Sintering Temperature: 850鈩
|